Honeycornb Ceramics, Monolith, High Alumina Porcelain Honeycomb manufacturer / supplier in China, offering Honeycomb Ceramic Heat Exchanger (Alumina Porcelain/Cordierite, Zta Ceramic Wear Liner, High Wear Resistance Aluminium Oxide Ceramic Block and Cubes Manufacturers and so on.
Min. Order / Reference FOB Price | |
---|---|
1 Ton | US $1999.00/ Ton |
Local Area: | Pingxiang, Jiangxi, China |
---|---|
R&D Capacity: | OEM, ODM, Other |
Payment Terms: | LC, T/T |
Material: | Alumina Ceramics |
---|---|
Content: | >90% |
Usage: | Chemical, Grind |
Alumina Grinding Ball
This product are featured by high density and hardness, low wear lost, corrosion-resistance etc. They are the perfect high-efficient grinding media for milling glaze/frit, pigment, ceramic materials, and various mine ore powder, they are using ceramics, cements, paints, refractories, inorganic mineral powders etc...
Applied for dry grinding , wet grinding ,mineral grinding , quartz grinding , lineston grinding , iron ore grinding , cement grinding , ceramics plants grinding , pigment grinding , mineral ore grinding , breaking platns .
Applied for ball mill,grinding machine , pot mill , librating mill , pebble mill , Attrition Mill,rod mill , grinding mill , grinding machine , ball grinding mill
Size:1mm, 3mm, 6mm, 9mm, 13mm, 16mm, 20mm, 25mm, 30mm , 40mm, 50mm, 60mm, 70mm,95mm
1: 92% Alumina content series
A) Al2O3 ≥ 92%
B) Water absorption <0.01%
C) Bulk density ≥ 3.63 g/cm3
D) Mosh hardness: 9
E) Color: White
2: 95% High-alumina grinding ball
A) Al2O3 ≥ 95% Sio2<3.8%, others:~3%
B) Water absorption <0.01%
C) Bulk density ≥ 3.7 g/cm3
D) Mosh hardness: 9
E) Color: White
F) Self abrasion loss : <0.008%
3: 68% Medium alumina grinding ball series :
A) Al2O3 : 65%~75%
B) Bulk density ≥ 2.93g/cm3
C) Mosh hardness: 8 grade
D) Self abrasion loss :0.01
E) Color : White or brown
ItemsProportionItemsProportionAl2O392%SiO2<6.5%others~2%
ItemsProportionItemsProportionHardness: Mohr's9self Abrasion Loss (24hour)<0.01%Density(g/cm3)3.6g/cm3Water Absorption<0.01%ColorWhiteBall methodBy cool isostatic-pressing Or by rolling
ItemsProportionItemsProportionAl2O395%SiO2<3%others~2%
ItemsProportionItemsProportionHardness: Mohr's9self Abrasion Loss (24hour)<0.01%Density(g/cm3)3.74g/cm3Water Absorption<0.01%ColorWhiteBall methodBy cool isostatic-pressing Or by rolling
ItemsProportionItemsProportionAl2O368.62%SiO221.2%others~10.18%
ItemsProportionItemsProportionHardness: Mohr's7-8Self Abrasion Loss (24hour)<0.03%Density(g/cm3)3.g/cm3Water Absorption<0.1%ColorCreamy whiteBall methodBy cool isostatic-pressing Or by rolling